A continuous solid nickel based electrode alloyed with 30 % Cu for welding of base materials of the same type. Can also be used to join these alloys to steel. The weld metal has good resistance to flowing seawater and has high strength and toughness over a rather wide temperature range. Has also good resistance to hydrofluoric acid, sulphuric acid, alkalis etc. Can be used for welding of similar types of base materials which are age-hardenable with small additions of Ti and Al. Usable for cladding on carbon steel with an intermediate layer of OK Autrod 19.92.
Approvals are based on factory location. Please contact ESAB for more information.
瑞典伊萨公司的历史是从1904年奥斯卡·卡尔伯格（Oscar Kjellbrg）先生发明药皮焊条开始的时至今日，伊萨的焊材仍然采用OK命名，使我们想起伊萨公司在焊接领域百年的发展壮大历程。
种类
ESAB
技术标准
熔敷金属力学性能
熔敷金属化学成分（％）
SFA/AWS
DIN 1736
屈服值Mpa
抗拉强度Mpa
延伸率％
冲击值
C
Si
Mn
Cr
Ni
Mo
其它
手工焊条
OK 92.05
A5.11 ENi-1
EL-NiTi3
320
450
25
0.05
1.0
0.7
－
92.0
－
Ti3.0
OK 92.15
A5.11
EL-NiCr15FeNb
420
660
45
+20 ℃ 110
＜ 0.1
0.5
2.0
15.5
70.0
2.0
Nb2.0
OK 92.26
A5.11-90
EL-NiCr15FeMn
410
640
40
+20 ℃ 100
＜ 0.1
0.6
6.0
16.0
70.0
－
Nb2.0
OK 92.45
A5.11
EL-NiCr20Mo9 Nb
480
800
40
+20 ℃ 70
＜ 0.03
0.4
0.4
22.0
64.0
9.5
Nb3.3
OK 92.55
A5.11
460
705
40
+20 ℃ 95
＜ 0.08
0.7
3.0
13.0
70.0
6.5
Nb1.3
OK 92.59
EL-NiCr22Mo16
430
不锈钢焊条
种类
ESAB牌号
技术标准
熔敷金属力学性能
熔敷金属化学成分（％）
SFA/AWS
EN
屈服值Mpa
抗拉强度Mpa
延伸率％
冲击值J
C
Si
Mn
Cr
Ni
其它
手工焊条
OK 61.25
A5.4-9E308-15
EN 1600E 19 9 H B 22
430
600
45
20℃ 70
0.06
0.5
1.7
18.5
9.5
－
OK 61.30
A5.4 E308L-17
EN 1600 E 19 9 L R 12
430
560
45
20℃ 70
0.03
0.8
0.7
19.5
10.0
－
OK 61.35
A5.4 E308L-15
EN1600E 19 9 L B 2 2
460
580
45
+20℃ 100-120℃ 70-196℃ 45
0.03
0.4
1.7
19.5
10.5
－
OK 61.41
A5.4 E308L-17
EN1600 E 19 9 L R 5 3
420
560
45
20℃ 65
0.03
0.7
0.8
19.5
10.0
－
OK 61.50
A5.4-92 E308H-17
EN1600 E 19 9 H R 12
430
600
45
20℃ 60
0.05
0.8
0.8
20.0
10.
－
OK 61.80
A5.4-92 E347-17
EN 1600E 19 9 Nb R 12
500
630
40
+20℃ 60-80℃ 40
0.03
0.7
0.6
20.0
10.0
Nb 0.3
OK 61.81
A5.4 E347-16
EN1600 E 19 9 Nb R 3 2
560
700
32
+20℃ 60
0.06
0.6
1.6
20.0
10.0
Nb 0.7
OK 61.85
A5.4 E347-15
EN1600 E 19 9 Nb B 2 2
500
620
40
+20℃ 100-60℃ 70
0.05
0.5
1.7
19.5
10.0
Nb 0.5
OK 61.86
A5.4 E347-17
EN1600 E 19 9 Nb R 1 2
520
660
35
+20℃ 55
0.03
0.7
0.8
19.0
10.0
Nb 0.3
OK 63.20
A5.4 E316L-16
EN1600 E 19 12 3 L R 1 1
480
580
35
+20℃ 65-60℃ 45-120℃ 32
0.03
0.7
0.8
18.5
12.0
Mo2.8
OK 63.30
A5.4 E316L-17
EN1600 E 19 12 3 L R 1 2
460
570
40
+20℃ 60-125℃ 32
0.03
0.8
0.6
18.0
12.0
Mo2.8
OK 63.31
A5.4 E316L-17
EN1600 E 19 12 3 L R 3 2
460
570
38
+20℃ 60-125℃ 35
0.03
0.8
0.7
19.0
11.0
Mo2.8
OK 63.34
A5.4 E316L-16
EN1600 E 19 12 3 L R 11
440
600
40
+20℃ 65
0.03
0.8
0.8
18.5
12.0
Mo2.8
OK 63.35
A5.4 E316L-15
EN1600E 19 12 3 L B 2 2
460
600
35
+20℃ 95-120℃ 60-196℃ 35
0.03
0.5
1.7
18.5
12.6
Mo2.8
OK 63.41
A5.4 E316L-17
EN1600 E 19 12 3 L R 5 3
430
570
45
+20℃ 60
0.03
0.8
0.7
18.0
12.0
Mo2.8
OK 63.80
A5.4 E318-17
EN 1600E 19 12 3 Nb R 3 2
500
620
35
+20℃ 55
0.02
0.8
0.6
18.0
12.0
Mo2.8Nb0.3
OK 64.30
A5.4 E317L-17
EN1600 E 19 13 4 LR 3 2
480
600
30
+20℃ 45
0.03
0.7
0.7
19.0
13.0
Mo2.8
OK 67.13
A5.4 E310-16
EN 1600 E 25 20 R 12
560
600
35
+20℃ 60
0.1
0.5
1.9
26.0
21.0
－
OK 67.15
A5.4 E310-15
EN 1600 E 25 20 B 22
410
590
35
+20℃ 100
0.1
0.3
2.0
26.0
20.0
－
OK 67.20
A5.4 E309MoL-16
EN1600 E 23 12 2 LR 1 1
480
640
35
+20℃ 60
0.03
0.8
0.8
23.0
13.0
Mo2.9
OK 67.50
A5.4 E2209-17
EN 1600E 22 9 3 N L R 3 2
660
820
25
+20℃ 70
0.03
0.8
1.0
23.0
9.0
Mo3.0N0.15
OK 67.55
A5.4 E2209-15
EN 1600E 22 9 3 N L B 2 2
650
800
28
+20℃ 100-40℃ 75-60℃ 65
0.03
0.7
1.0
23.0
9.0
Mo3.0N0.15
OK 67.60
A5.4 E309L-17
EN 1600E 23 12 L R 3 2
470
580
32
+20℃ 50-10℃ 40
0.03
0.8
0.9
24.0
12.5
－
OK 67.62
A5.4 E309-26
EN1600 E 23 12 R 7 3
450
570
40
+20℃ 60
0.05
0.8
0.6
24.0
12.5
－
OK 67.66
A5.4 E309L-16
EN1600 E 23 23 L R 3 2
430
580
45
+20℃ 70
0.03
0.4
1.0
23.0
13.0
－
OK 67.70
A5.4 E309MoL-17
EN1600 E 23 12 2 LR 3 2
510
620
33
+20℃ 50
0.03
0.8
0.6
23.0
13.0
Mo2.7
OK 67.75
A5.4 E309L-15
EN1600 E 23 12 L B 4 2
460
570
35
+20℃ 75-80℃ 55
0.03
0.3
0.2
24.0
13.0
Mo0.3
OK 68.15
A5.4 E410-15
EN1600 E 13 B 4 2
390
520
25
+20℃ 55
0.06
0.5
0.5
13.0
－
－
OK 68.17
A5.4 E410NiMo-16
EN 1600E 13 4 R 3 2
650
870
17
+20℃ 45-10℃ 45-40℃ 40
0.03
0.4
0.6
12.0
4.6
Mo0.6
OK 68.25
A5.4E410NiMo-15
EN 1600E 13 4 B 4 2
680
880
17
+20℃ 60-20℃ 53
0.03
0.4
0.6
12.5
4.5
Mo0.6
OK 68.60
EN 1600 E 25 4 R 3 2
660
800
15
+20℃ 30
0.05
1.1
1.2
26
5
Mo1.5N0.18
OK 68.81
A5.4 E312-17
EN1600 E 29 9 R 3 2
580
750
25
+20℃ 30
0.12
0.7
0.8
29.0
10.0
－
OK 69.25
EN 1600E 20 16 3 Mn L B 4 2
450
650
30
+20℃ 90-196℃ 50
0.03
0.5
6.5
19.0
16.0
Mo3.0N0.15
OK 69.33
A5.4E385-16
EN 1600E 20 25 5 Cu N L R 3 2
400
575
35
+20℃ 80-140℃ 45
0.03
0.5
1.0
20.5
25.0
Mo5.0Cu1.5
低合金钢焊条
种类
ESAB
技术标准
熔敷金属力学性能
熔敷金属化学成分（％）
SFA/AWS
EN
屈服值Mpa
抗拉强度Mpa
延伸率％
冲击值
C
Si
Mn
Ni
Cr
Mo
手工焊条
OK 48.08
A5.5-96 E7018-G
EN 499
540
600
26
-20 ℃ 160
0.06
0.35
1.2
0.9
－
－
OK 73.15
A5.5
EN 499
550
610
28
-50 ℃ 120
0.06
0.4
1.4
0.9
－
－
OK 73.68
A5.5
EN 499
520
610
26
-55 ℃ 110
0.05
0.35
1.0
2.4
－
－
OK 73.79
A5.5
EN 499
520
610
26
-60 ℃ 160
0.06
0.3
0.6
3.3
－
－
OK 74.46
A5.5
EN 1599
460
560
27
+20 ℃ 175
0.06
0.3
0.8
－
－
0.5
OK 74.70
A5.5
EN 499
540
630
26
-20 ℃ 110
0.08
0.4
1.5
－
－
0.4
OK 74.78
A5.5
EN 1599
600
650
24
0 ℃ 100
0.06
0.35
1.5
－
－
0.35
OK 75.75
A5.5 E11018-G
EN 757
755
820
20
-20 ℃ 85
0.05
0.35
1.75
2.25
0.45
0.45
OK 75.78
EN757 E89 6 Mn3NiCrMo B 42 H5
920
965
17
-60 ℃ 60
0.05
0.3
2.1
3.1
0.5
0.6
OK 76.18
A5.5 E8018-B2
EN 1599
530
620
20
+20 ℃ 120
0.06
0.3
0.7
－
1.3
0.5
OK 76.28
A5.5
EN 1599
550
650
18
+20 ℃ 120
0.06
0.3
0.7
－
2.3
1.1
OK76.35
A5.5
EN 1599
/
460
35
+20 ℃ 145
0.05
0.4
0.7
－
5.0
0.55
OK 76.96
A5.5 E8015-B8
EN 1599 E CrMo 9 B
/
＞ 450
＞ 20
+20 ℃＞ 80
0.05
0.5
0.8
－
9.5
1.0
OK 78.16
A5.5 E9018-G
870
900
18
规格
Consumable Characteristics
Alloy Type
Alloyed nickel (Ni + 30 % Cu + 2 % Ti + 2 % Fe)
分类
ERNiCu-7
SFA/AWS A5.14
S Ni 4060 (NiCu30Mn3Ti)
EN ISO 18274
焊缝金属分析
Analysis Type
3
元素
C
额定百分比
0.03 %
Analysis Type
3
元素
Si
额定百分比
0.3 %
熔敷数据
安培
100-200 A
熔敷率
2,5-5,5 kg/h
电压 V
21-27 V
直径
1.0 mm
送丝速度
6-13 m/min
分类:
ERNiCu-7,SFA/AWS A5.14,S Ni 4060 (NiCu30Mn3Ti),EN ISO 18274
认证:
01554 (MV),VdTÜV,06276 (FP),VdTÜV
Alloy Type:
Alloyed nickel (Ni + 30 % Cu + 2 % Ti + 2 % Fe)
熔敷数据
安培
熔敷率
电压 V
直径
送丝速度
As welded
100-200 A
2,5-5,5 kg/h
21-27 V
1.0 mm
6-13 m/min
品牌：瑞典伊萨
伊萨公司悠久的历史和不断发展壮大的努力使得伊萨公司成为焊接和切割领域****的公司。
伊萨公司的第一个发明是药皮焊条。随之而来的是伊萨在全世界的工程师们为工业界带来无数发明创造。其中包括一些焊接领域重要的突破，如挤压药皮焊条、埋弧焊（Unionmelt）、铁粉低氢焊条，MIG焊、TIG焊（Heliarc）、第一个使用气体保护药芯焊丝（Dualshield）第一个使用全位置药芯焊丝、等离子切割和焊接以及其他一些对焊接质量和提高生产率有重大影响的方法。时至今日，伊萨公司仍然是焊接新产品、新工艺的倡导者，如摩擦搅拌焊，独特的药芯焊丝焊接铸铁，高强焊丝焊接特殊的高强钢。伊萨这种保持领先的传统使其成为您在焊接和切割方面的最佳伙伴。
镍基合金焊条
牌号
J
Fe0.7
EniCrFe-2
-196 ℃ 90
Fe8.0
EniCrFe-3
-196 ℃ 80
Fe6.0
EniCrMo-3
-196 ℃ 50
Fe3.0
ENiCrMo-6
-60 ℃ 90
-196 ℃ 80
Fe4.0
W1.5
牌号
J
E 46 5 1 Ni B 32 H5
-40 ℃ 130
-50 ℃ 100
-60 ℃ 60
E7018-G
E 46 5 Mn 1Ni B 42 H5
E8018-C1
E 46 6 2Ni B 32 H5
-60 ℃ 105
E8016-C2
E 46 6 3Ni B 12
-73 ℃ 90
-95 ℃ 40
-101 ℃ 35
E7018-A1
E Mo B 42
-20 ℃ 100
E8018-G
E 46 MnMo B 32
-40 ℃ 80
-60 ℃ 50
E9018-D1
E Mo B42
-20 ℃ 90
-30 ℃ 75
-40 ℃ 60
E 69 5 Mn2 NiCrMoB 42 H5
-40 ℃ 70
-51 ℃ 55
-60 ℃ 45
E CrMo 1 B 42 H5
E9018-B3
E CrMo 2 B 42 H5
E8015-B6
E CrMo 5 B 32 H5
-20 ℃ 75