Jupiter-AAA铸铁焊条

Shield Metal Arc Welding(SMAW - Stick)

手工焊条电弧焊（SMAW-Stick）

For all cast irons - Meehanite, ductile, mealleable, gray cast irons and steel to cast iron.

适用于所有铸铁-Meehanite孕育铸铁、球墨铸铁、可锻铸铁、灰口铸铁，以及钢至铸铁的焊接。

Features

亮点

High Strength Up To 70,000psi/482MPa

抗拉强度高达70,000psi/482MPa

No Electrode Overheating

无焊条过热

Smooth Ductile Deposits

平滑韧性熔敷层

Steel To Cast Iron

钢和铸铁的焊接

More Efficient Deposits

更高效的熔敷

All Weldable Grades Of Cast Iron

所有可焊接等级的铸铁

Machinable Deposit

可加工熔敷层

Eliminates Porosity

无气孔

Characteristics

Jupiter AAA is engineered to give the user a high strength ductile weld without electrode overheating, thus producing a much more efficient deposit that is machinable. Welds are typically smooth, porosity free and flat. Excellent tie in between passes.

Jupiter AAA的设计目的是为用户提供高强度的韧性焊缝，而不会使焊条过热，从而更高效的产生可加工的熔敷层。焊缝通常光滑、无气孔且平整。出色的焊道间结合。

Jupiter AAA makes it easier and more cost effective to do large cast iron repairs. It can be used on dirty and oil impregnated pieces without the problem of electrode overheating. Superior choice for joining cast iron to steel.

Jupiter AAA使大型铸铁维修变得更容易、更具成本效益。它可以用于脏的和含油浸的工件，而不会出现焊条过热的问题。铸铁与钢连接的理想选择。

Technical技术参数

Size and Amps AC/DC+(DCEP)

Best Practices Application 应用

Remove cracks using grinder or Electra.

去除裂缝.

Stop drill cracks ends.

止裂孔。

Use medium arc and stringer beads.

使用中等弧长和线状焊道。

Skip weld, light peening recommended.

跳焊，建议轻敲击。

For critical or heavy parts preheat to 500⁰F(260⁰C).

对于关键或重型零件，预热至500⁰F(260⁰C)。

Cool slowly after welding. 焊后缓冷。