Jupiter A铸铁焊条

Shield Metal Arc Welding(SMAW - Stick)

For all Cast Iron - Meehanite,ductile, mealleable, gray cast irons and steel to cast iron.

适用于所有铸铁-Meehanite孕育铸铁、球墨铸铁、可锻铸铁、灰口铸铁和钢至铸铁的焊接。

Features

亮点

High Strength 79,000psi/545MPa

抗拉强度高达79,000psi/545MPa

Use On All Weldable Grades Of Cast Iron

用于所有可焊接等级的铸铁

All positions

全位置焊接

Welds Over Dirt and Oil

可以在油污上直接焊接

Eliminates Porosity

无气孔

Ideal For Cast Iron To Steel Joining

铸铁与钢连接的理想选择

Prevents Hard Spots

不会出现硬点

Easy To Use

易于使用

Machineable deposits

可加工熔敷层

Welds Over Slag

熔渣上的焊缝

Ductile Deposits

韧性熔敷层

No preheat required

不需要预热

Characteristics

特点

Jupiter-A has been engineered for the maintenance welder who must weld dirty, oil-soaked castings of unknown compositions. Sound, non-porous welds are produced without special preparation. Successful results are possible even when the joint is restrained.

Jupiter-A专为必须焊接成分未知的脏、浸油铸件的维护焊工设计。在无需特殊处理的情况下，即可产生完好、无孔的焊缝。即使接头受到约束，也有可能取得成功。

Jupiter-A makes it possible to repair machines and equipment in place without expensive tear down, thereby avoiding costly down time.

Jupiter-A可以在不需要拆卸的情况下将机器和设备维修到位，从而避免了高成本的停机时间。

Technical技术规格

Size and Amps AC/DC+(DCEP)

Best Practices Application 应用

Remove cracks using grinder or Electra去除裂缝。

Stop drill crack ends.实施止裂孔。

Use medium arc and stringer beads. 使用中等弧度和线状焊道。

Skip weld and prevent overheating 跳焊并防止过热

Light peening recommended. 建议进行轻敲击。

For critical or heavy parts preheat to 500⁰F(260⁰C). 对于关键或重型零件，预热至500⁰F（260⁰C）。

Cool slowly after welding. 焊后缓冷。