英国进口MWA铸铁焊条Mac Cast E407|ENiFe-CI|铸铁焊接|压力容器焊接

High strength machinable electrode for joining and building up on cast irons. Low amperage, smooth arc, minimum spatter and high resistance to cracking. Due to Bi-bllic core wire this product gives excellent current carrying capacity which will prevent overheating. For the repair of grey, S.G., nodular or ductile irons where higher strength is required. Also suitable for joining cast iron to mild steel (in conjunction with Mac Groove 71), pressure vessels, etc. Also available as a MIG wire.

高强度可加工Ni55镍铁焊条，用于铸铁的连接和堆焊。电流低，电弧平滑，飞溅小，抗裂性高。由于双金属芯线，该产品具有出色的载流能力，可防止过热。用于需要更高强度的灰口铸铁、球墨铸铁的修复。也适用于连接铸铁和低碳钢（与Mac Groove E71切割焊条一起使用）、压力容器等。有对应MIG焊丝可供选择。

典型应用：发动机缸体、气缸盖、泵壳、电机外壳、齿轮箱、机器底座、法兰、凸轮、杆类、填充孔、铸造轮齿修复以及堆焊或更换缺失部分。

Typical All Weld Metal Chemical Analysis (%)

典型全焊缝金属成分

Typical All Weld Metal Mechanical Properties（As Welded）

典型全焊缝金属机械性能（焊态）：

Tensile Strength抗拉强度： 448 N/mm²

Elongation延伸率： 20%

Hardness硬度： 180 HB

Sizes Available and Recommended Amperages

尺寸Φ/电流：

Current电流：AC/DC (+)

Related Specification参考标准：AWS A5.15 ENiFe-CI

Storage储存：Electrodes should be stored in dry conditions. Should the electrodes become damp, re-dry for one hour at 150°C before use. 焊条应储存在干燥环境中。如果焊条受潮，应在150°C下重新干燥1小时后再使用。

使用注意事项：

如有可能，清洁焊接区域。去除表皮和所有锐边。确保施焊部位没有油污等。

推荐采用“U”坡口接头。

使用3mm钻头在裂缝末端钻孔，以防止焊接过程中进一步扩展。

从裂缝的末端开始焊接，向内焊接。

使用低电流并保持短弧。

应使用短线状焊道(2-3cm)或窄编织焊道，以防止过热。

采用直流焊机时根据熔敷情况改变正负极。

断开电弧时，始终填充弧坑，并将焊条拉回到焊缝熔敷层上。

趁热锤击将有助于降低收缩应力。

重新引弧时，电弧从先前沉积的焊缝金属开始，而不是从母材开始。

让零件慢慢冷却。