8407-H13焊丝
| 特 性 |
焊金耐热 耐腐蚀 耐磨耗性能优良,用于修复基体合金相似的高温加工工具,如H13钢.
硬度HRC 43～46度A hot work tool steel that is tungsten free,Good hot hardness up to 565℃.For repair of H-13 tool steels and appications in the die casting and forging industries subject to high thermal gradients.
|
| 用 途 |
焊补有色金属压铸模具 PA POM PS PE EP Weld-repair non-ferrous bl die-casting molds PA POM PS PE EP
|
| 规 格 | 1.0￠ 1.2￠ 1.6￠ 2.0￠ 2.4￠ |
| 特 性 |
马氏体时效钢,其堆焊层硬度可达HRC30～32度,溶敷金属柔软,具韧性易切削,在其500℃/2H时效处理后硬度可提高到HRC48～50度. Limitation of martensite steel, the hardfacing layer of hardness HRC30 ~ 32 degrees, soluble bl soft, apply, in its toughness cutting 500 ° c / 2H aging treatment can improve HRC48 hardness to 50 ~.
|
| 用 途 |
焊补铝压铸模具,挤压模具,冲裁模 注塑模等. Weld repairs, aluminum casting die, extrusion dies, punching mould injection mold, etc
|
| 规 格 | 1.0￠ 1.2￠ 1.6￠ 2.0￠ |
| 特 性 |
含有W Mo Cr V 的高合金焊丝,溶敷金属具有高韧性,高硬度冲击耐磨耗性能,可使用在600℃的热间环境,焊后金属可高达HRC61～63度,经热处理后硬度尚有提高. Contains W Mo Cr V high alloy welding wire, soluble deposited bl with high toughness and high hardness, impact abrasion resistance perbance can be used in 600 degrees Celsius between thermal environment, after welding bl can be as high as HRC61 ~ 63 degree of hardness, still improve.
|
| 用 途 |
焊补冷热作模具,成型刀具,修整刀具 冲头 模具 粉碎机刃口,冲压模具,也可以在碳钢和低合金钢上堆焊制成新工具. Heat for mould weld-repair, molding tool, die cutter punch grinder blade, stamping, also can be in the carbon steel and the low alloy steel made on new tools. #
|
| 规 格 | 1.0￠ 1.2￠ 1.6￠ 2.0￠ |
| 特 性 |
氩弧焊铜 优异的机械加工性能 硬度HB-200. Argon arc welding copper excellent machining perbance hardness HB - 200.
|
| 用 途 |
广泛用于电解片 铜合金 钢 青铜 生铁铜件之焊补. Widely used in electrolytic copper alloy steel cast bronze pieces of copper pieces of weld-repair.
|
| 规 格 | 0.9￠ 1.2￠ 1.6￠ 2.0￠ |
| 特 性 |
以焊接开裂敏感性低的合金成份设计,含镍约1%机械加工性能与蚀刻性优越,焊后硬度
HRC30~34. n cracking sensitivity low alloy welding components design, containing nickel about 1% of machining perbance and etching of superior, postweld hardness
HRC30 ~ 34.
|
| 用 途 |
塑胶模具的焊补. Plastic mould weld-repair.
|
| 规 格 | 0.9￠ 1.2￠ 1.6￠ 2.0￠ |