| PA66 408L 美国杜邦公司 物性数据 |
| 规格级别： | 特殊级 | 外观颜色： | --- |
| 用途概述： | 适合超高抗冲击性的工程制品 | ||
| 备注说明： | --- | ||
| 性能项目 | 试验条件[状态] | 测试方法 |
|
数据单位 | |||||
| 基本性能 | 吸水率 | 24hr | ASTM D-570 | 1.2 | % | ||||
| 物理性能 | 模具收缩率 | 3.2mm | --- |
|
% | ||||
| 阻燃性 | --- | UL 94 |
|
mm | |||||
| 比重 | --- | ASTM D-792 |
|
--- | |||||
| 阻燃性 | --- | UL 94 | HB | --- | |||||
| 机械性能 | 拉伸强度 | 23℃ | ASTM D-638 |
|
MPa | ||||
| 拉伸屈服强度 | --- | ASTM D-638 |
|
MPa | |||||
| 断裂伸长率 | --- | ASTM D-638 |
|
% | |||||
| 屈服伸长率 | --- | ASTM D-638 |
|
% | |||||
| 弯曲模量 | --- | ASTM D-790 |
|
MPa | |||||
| IZOD冲击强度 | --- | ASTM D-256 |
|
J/m | |||||
| 电气性能 | 体积电阻率 | --- | ASTM D-257 |
|
Ω.cm | ||||
| 热 性 能 | 熔点 | --- | ASTM D-3418 |
|
℃ | ||||
| 热变形温度 | 0.45MPa | ASTM D-648 |
|
℃ | |||||
| 热变形温度 | 1.80MPa | ASTM D-648 |
|
℃ | |||||
| 其它性能 | CLTE | --- | ASTM D-696 |
|
10-4/K | ||||