| 密度 | 0.9 | g/cm | ASTM D-1505 |
| 熔体流动速率 (230℃) | 20 | g/10min | ASTM D-1238 |
| 洛氏硬度 | 96 | R | ASTM D-785 |
| IZOD冲击强度 (-10℃) | 4.0 | Kg·cm/cm | ASTM D-256 |
| 伸长率 | >100 | % | ASTM D-638 |
| 弯曲模量 | 14,500 | Kg/cm | ASTM D-790 |
| 拉伸屈服强度 | 270 | Kg/cm | ASTM D-638 |
| IZOD冲击强度 (23℃) | 7.0 | Kg·cm/cm | ASTM D-256 |
| Du-Pont冲击强度 (-10℃) | 45 | HPC Method |
| 热变形温度 (4.6MPa) | 114 | ℃ | ASTM D-648 |