| PBT 4115 台湾长春企业集团 物性数据 |
| 规格级别： | 强性难燃级 | 外观颜色： | 黑色本色 |
| 用途概述： | 连接器、冷却风扇、插座、线圈轴、汽机车零件、开关、电视机零件、整流器。 | ||
| 备注说明： | 含有玻纤15%，强度大，难燃等级达1/32inch,UL94V-0,成型容易 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸水率 | --- | ASTM D-570 | 0.03 | % |
| 物理性能 | 成型收缩率 | --- | ASTM D-955 | 0.4-0.2 | % |
| 比重 | --- | ASTM D-792 | 1.50-1.52 | - | |
| 玻璃纤维含量 | --- | Ash | 15 | % | |
| 机械性能 | 引张强度 | --- | ASTM D-638 | 900-1100 | Kg/cm2 |
| 引张伸长率 | --- | ASTM D-638 | 4-5.5 | % | |
| 挠曲强度 | --- | ASTM D-790 | 1400-1800 | Kg/cm2 | |
| 挠曲弹性率 | --- | ASTM D-790 | 45000-65000 | Kg/cm2 | |
| IZOD冲击强度 | --- | ASTM D-256 | 5-7 | Kg.cm/cm | |
| 洛氏硬度 | --- | ASTM D-785 | 93 | M-Scale | |
| 电气性能 | 诱电率 | 60Hz | ASTM D-150 | 3.3 | --- |
| 诱电正接 | 60Hz | ASTM D-150 | 0.001 | --- | |
| 体积电阻率 | --- | ASTM D-257 | >1016 | Ω.cm | |
| 表面电阻率 | --- | ASTM D-257 | >1014 | Ω | |
| 绝缘破坏强度 | --- | ASTM D-149 | 22 | KV/mm | |
| 耐电弧性 | --- | ASTM D-495 | 90 | sec | |
| 热 性 能 | 耐燃性 | 0.75mm | UL 94 | V-0 | - |
| 热变形温度 | 4.6Kg/cm2 | ASTM D-648 | 220 | ℃ | |
| 线膨胀系数 | --- | ASTM D-696 | 5.5 | 10-5cm/cm℃ | |
| 熔点 | --- | DSC | 225 | ℃ | |
| 热变形温度 | 18.6Kg/cm2 | ASTM D-648 | 205 | ℃ | |
本公司长期经营各品牌PA66塑胶原料，质量保证，欢迎咨询洽谈13694927883蒋先生
供应PA66，FR7025V0F,FR7026V0F美国杜邦阻燃热稳定未增强无卤；（新加坡杜邦）
3.供应PA66，A3K，A3Z增韧级德国巴斯夫未增强；
供应PA66，A3X2G5,A3X2G7红磷阻燃玻纤增强德国巴斯夫；
供应PA66，A3EG3,A3EG5,A3EG6，A3EG7,A3EG10玻纤增强级德国巴斯夫；（上海/马来西亚巴斯夫）
供应PA66，A3WG6,A3WG3,A3WG5,A3WG10玻纤增强级德国巴斯夫；（上海/马来西亚巴斯夫）
供应PA66，A30S非增强热稳定德国朗盛(拜耳)；
供应PA66，A3HG5，A3HG6，A3HG7玻纤增强级德国巴斯夫热稳定；
4.供应PA66，CM
供应PA66，CM3006G-30，CM3006G-45，CM3006G-15玻纤增强日本东丽热稳定；
供应PA66，CM3004G-30，CM3004G-20，CM3004G-15含卤素阻燃级玻纤增强日本东丽；
供应PA66，CM3004-V0无卤阻燃未增强日本东丽；
供应PA66，CM3006耐热级未增强日本东丽；
供应PA66，CM3001-N标准级未增强日本东丽V2；
供应PA66,AG-30/10日本EMS高耐磨耐冲耐高温(GF30,铁氟龙10)；
5.供应PA66,1300S未增强日本旭化成（垫圈电线绑扎带）；
供应PA66,1300G玻纤增强日本旭化成V2阻燃注塑级（33GF）；