| PBT 4130F 台湾长春企业集团 物性数据 |
| 规格级别： | 强化难燃级 | 外观颜色： | --- |
| 用途概述： | --- | ||
| 备注说明： | --- | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |||||||||||
| 物理性能 | 比重 | --- | ASTM D792 | 1.62-1.68 | --- | ||||||||||
| 吸水率 | 24hr immersion | ASTM D570 | 0.03 | % | |||||||||||
|
|
|
|
| |||||||||||
| 玻璃纤维含量 | --- | Ash | 30 | % | |||||||||||
| 机械性能 | 引张强度 | --- | ASTM D638 | 1100-1400 | kg/cm2 | ||||||||||
| 引张伸长率 | --- | ASTM D638 | 2.5-4.5 | % | |||||||||||
| 挠曲强度 | --- | ASTM D790 | 1500-2300 | kg/cm2 | |||||||||||
| 挠曲弹性率 | --- | ASTM D790 | ≥70000 | kg/cm2 | |||||||||||
| IZOD冲击强度 | 切口1/4″ | ASTM D256 | 7-13 | kg-cm/cm | |||||||||||
| 硬度 | --- | ASTM D785 | 94 | M-Scale | |||||||||||
| 电气性能 | 诱电率 | --- | ASTM D150 | 3 | 60Hz | ||||||||||
| 诱电正接 | --- | ASTM D150 | 0.001 | 60Hz | |||||||||||
| 体积抵抗率 | --- | ASTM D257 | ＞1015 | Ω-cm | |||||||||||
| 表面抵抗率 | --- | ASTM D257 | ＞1013 | Ω | |||||||||||
| 绝缘破坏强度 | 2mm | ASTM D149 | ＞20 | KV/mm | |||||||||||
| 耐电弧性 | --- | ASTM D495 | 100 | sec | |||||||||||
| 热 性 能 | 线膨胀系数 | --- | ASTM D696 | 3 | 10-5cm/cm℃ | ||||||||||
| 耐燃性 | 0.8mm | UL94 | V-0 | --- | |||||||||||
| 融点 | --- | DSC | 225 | ℃ | |||||||||||
| 热变形温度 | 18.6kg/cm2(4.6kg/cm2) | ASTM D648 | 208（220） | ℃ | |||||||||||
供应PA66，FR7025V0F,FR7026V0F美国杜邦阻燃热稳定未增强无卤；（新加坡杜邦）
3.供应PA66，A3K，A3Z增韧级德国巴斯夫未增强；
供应PA66，A3X2G5,A3X2G7红磷阻燃玻纤增强德国巴斯夫；
供应PA66，A3EG3,A3EG5,A3EG6，A3EG7,A3EG10玻纤增强级德国巴斯夫；（上海/马来西亚巴斯夫）
供应PA66，A3WG6,A3WG3,A3WG5,A3WG10玻纤增强级德国巴斯夫；（上海/马来西亚巴斯夫）
供应PA66，A30S非增强热稳定德国朗盛(拜耳)；
供应PA66，A3HG5，A3HG6，A3HG7玻纤增强级德国巴斯夫热稳定；
4.供应PA66，CM
供应PA66，CM3006G-30，CM3006G-45，CM3006G-15玻纤增强日本东丽热稳定；
供应PA66，CM3004G-30，CM3004G-20，CM3004G-15含卤素阻燃级玻纤增强日本东丽；
本公司长期经营各品牌PA66塑胶原料，质量保证，欢迎咨询洽谈：13694927883