| 规格级别 | 其它 其它 阻燃 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | 特性：阻燃，流动性改良 | ||
| 加工条件 |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 模具收缩率 | 3.2mm | ASTM D-955 | 4-6 | E-3 |
| 吸水率 | ASTM D-570 | 0.1 | % | ||
| 比重 | ASTM D-792 | 1.18 | |||
| 机械性能 | 洛氏硬度 | ASTM D-785 | 121 | R | |
| 拉伸强度(屈伏点) | ASTM D-638 | 64 | Mpa | ||
| 拉伸模量 | ASTM D-638 | - | Mpa | ||
| 弯曲强度 | ASTM D-790 | 96 | Mpa | ||
| 冲击强度缺口 | 23℃ | ASTM D-256 | 453 | J/m | |
| 弯曲模量 | ASTM D-790 | 2584 | Mpa | ||
| 拉伸率(断裂点) | ASTM D-638 | 40 | % | ||
| 电气性能 | 体积电阻 | ASTM D-257 | 2.0E+17 | Ohm-cm | |
| 损耗因数 | 1MHz | ASTM D-150 | 0.0071 | ||
| 介电常数 | 1MHz | ASTM D-150 | 2.7 | ||
| 表面电阻 | ASTM D-257 | 1.0E+16 | Ohm-cm | ||
| 热性能 | 维卡软化点 | ASTM D-1525 | 112 | ℃ | |
| 阻燃性 | UL-94 | V-0 | |||
| UL长期使用温度 | 无冲击 | UL-746B | 85 | ℃ | |
| 线膨胀系数 | E831 | - | 1/℃ | ||
| 热变形温度 | 1.8Mpa | ASTM D-648 | 93 | ℃ | |
| 热变形温度 | 0.45Mpa | ASTM D-648 | 101 | ℃ | |
| UL长期使用温度 | 含冲击 | UL-746B | ℃ | ℃ | |
| 阻燃性 | UL-94 | 1.6 | mm | ||