The primary use of ERNiCrFe-6 is for clading steel with nickel-chromium-iron weld bl and | ||||||
| for joining sbl and stainless sbl to nickel-base alloys.Weld deposits can be age- hardened | ||||||
| with the degree of hardness depending on the time and temperature. | ||||||
| CLASSIFICATIONS: | ||||||
| ERNiCrFe-6 | ||||||
| AWS A5.14 | ||||||
| ASME SFA 5.14 | ||||||
| UNS N07092 | ||||||
| APPROVALS: | ||||||
| MIL-E-21562E | ||||||
| MIL-EN/RN6A | ||||||
| APPLICATIONS: | ||||||
| ERNiCrFe-6 is well suited for applications requiring superior corrosion resistance from | ||||||
| cryogenic to elevated temperatuers (up to 1800°F). Typical examples include power genera- | ||||||
| tion and petrochemical plants and fur- nace equipment. | ||||||
| DIAMETERS: | ||||||
| 0.035'', 0.045'', 0.063'', | ||||||
| 3/32'', 1/8'', 5/32'', | ||||||
| 3/16'' | ||||||
| TYPICAL | ||||||
| MECHANICAL PROPERTIES: | ||||||
| TENSILE STRENGTH(PSI) 80,000 | ||||||
| PERCENT ELONGATION 30 | ||||||
| TYPICAL | ||||||
| CHEMICAL COMPOSITION: | ||||||
| C | Mn | P | S | Si | Ni | |
| 0.05 | 2.40 | 0.001 | 0.001 | 0.17 | 70.40 | |
| Cr | Fe | Ti | ||||
| 16.50 | 7.50 | 2.80 | ||||