电解碳化钨粉
Electrolysis Tungsten Carbide Powder
一、典型应用Typical Applications
电解碳化钨是将废合金通过电解工艺生产出来的再生碳化钨原料。 由于钨资源有限，目前国家已经开始调控，电解碳化钨因为其生产能耗低，原料的适应面广，对于资源的再利用具有重要意义。
主要应用于，硬质合金，超硬材料，金刚石工具，焊接，耐高温材料，钻头，各种硬质合金刀具。
Electrolysis tungsten carbide is produced through the electrolysis process quality recycled scrap tungsten carbide materials. Electrolysis is low energy consumption, wide adaptability of raw materials, and great significance for the resource utilization.
Widely used in tungsten carbide, super-hard materials, diamond tools, welding, high temperature materials, drill bits, cutting tools etc.
二、主要物理特性Main Physical Specifications
过筛粒度/Particle Size: 60~325目(Mesh) 霍尔流速/Hall Flow Rate: 9~12 S/50g
松装密度/Apparent Density: >6.8g/cm3 费氏粒度（FSSS）: 0.8~10.0μm
振实密度/Vibrating Density: >8.2g/cm3 外观/Appearance: 深灰色/Dark Grey
|
牌号Grade |
EWC20 |
EWC50 |
EWC90 |
EWC10 |
|
|
主要成分（%） Main Contents |
总碳 Total C |
5.95~6.05 |
5.95~6.10 |
6.0~6.15 |
5.95~6.05 |
|
游离碳Free C |
0.05 |
0.05 |
0.04 |
0.04 |
|
|
杂质含量%不大于 Impurity Content % Max |
O |
0.5 |
0.15 |
0.15 |
0.15 |
|
Ti |
0.5 |
0.1 |
0.05 |
0.05 |
|
|
Co |
0.3 |
0.3 |
0.3 |
0.3 |
|
|
费氏粒度(FSSS) |
1.6~3.2μm |
4.5~6.0μm |
8.0~10.0μm |
0.8~1.7μm |
|
|
推荐用途 Recommended Applications |
用途生产普通YG类，或者YT类硬质合金产品
|
中颗粒度较粗的产品，适合大多数硬质合金产品应用 |
粗颗粒，主要应用于地矿产品，如钎片 |
细颗粒，可以用于要求较高的硬质合金产品，如圆棒、刀具等精加工产品 |
|
包装：内衬两层塑料袋、外铁桶，每桶50kg。
注：如客户另有特殊要求，可具体洽谈。Note：Another special requirements, specific negotiations