| EN ISO 3581-A. |
| E 19 12 3 L B 2 2 |
| SFA/AWS A5.4 |
| E316L-15 |
| 测试温度(焊态) | +20 °C |
| 结果(焊态) | 95 J |
| 测试温度(焊态) | -60 °C |
| 结果(焊态) | 75 J |
| 伸长率(焊态) | 30 % |
| 屈服强度(焊态) | 430 MPa |
| 抗拉强度(焊态) | 520 MPa |
| 电流类型 CA/CD/CC (+)(-) | DC+ |
| 硬度 (HRC) | 190-215 HV |
| 元素 | C |
| 额定百分比 | 0.04 % |
| 元素 | Si |
| 额定百分比 | 0.45 % |
OK 63.35 is a low carbon stainless steel electrode with basic coating of the 18Cr12Ni3Mo type. It is suitable for applications where the mechanical requirements are tough. It provides good impact toughness levels. Minimum lateral expansion of 0.38mm requirement is met down to -120°C. The same requirement can be met at -196°C when the ferrite content is at the low end of the specification i.e. FN 3 - 4.