安徽合肥铝合金牺牲阳极厂家批发Anhui Hefei aluminum alloy sacrifice anode manufacturers wholesale
Chemical Comb:
Type
Al
Zn%
In%
Cd%
Sn%
Mg%
Ti%
Impurity is not
greater than
Si
Fe
Cu
Al-Zn-In
remainder
2.0-6.0
0.01-0.02
--
--
--
--
0.10
0.15
0.01
Al-Zn-In-Cd
remainder
2.5-4.5
0.018-0.050
0.005-0.020
--
--
--
0.10
0.15
0.01
Al-Zn-In-Sn
remainder
2.2-5.2
0.20-0.045
--
0.018-0.035
--
--
0.10
0.15
0.01
Al-Zn-In-Si
remainder
5.5-7.0
0.025-0.035
--
--
--
--
0.10
0.15
0.01
Al-Zn-In-Sn-Mg
remainder
2.5-4.0
0.020-0.050
--
0.025-0.075
0.50-1.00
--
0.10
0.15
0.01
Al-Zn-In-Mg-Ti
remainder
4.0-7.0
0.020-0.050
--
--
0.50-1.50
0.01-0.08
0.10
0.15
0.01
Electrochemical Property :
Type
Open circuit potential
（-V CSE)
Closed circuit potential
（-V CSE)
Capacitance
A·h/kg
Current efficiency %
Surface dissolving
AL1
1.10-1.18
1.05-1.12
2400min
85min
unibity
AL2
1.10-1.18
1.05-1.12
2600min
90min
unibity
AL3
1.45-1.50
1.40-1.45
2080min
70min
unibity
阳极表面质量
1 牺牲阳极的工作表面可为铸造面。
2 牺牲阳极工作面应无氧化渣，毛刺，飞边，等缺陷，牺牲阳极所有表面允许长度不超过50mm,深度不超过5mm 横向细裂纹存在，但不允许有裂纹团存在。
3 牺牲阳极工作面允许有铸造孔，但其深度不得超过阳极厚度的10%，深度不得超出10mm。
4 牺牲阳极工作面应保持干净，不得沾有油漆和油污等。
阳极铁脚
1 板状铁脚
采用钢筋碳素结构钢制造。钢板的成分和尺寸应符合 GB／T 700 的规定。
2 钢管铁脚
采用无缝钢管制造。钢管成分的尺寸应符合 GB／T 17395 的规定。
3 螺纹钢铁脚
采用月牙钢筋制造。钢筋的成分，尺寸及外形应符合 GB 1499 的规定。
4 圆钢铁脚
采用钢筋制造。钢筋的成分和尺寸应符合 GB 1499 的规定。
5 表面处理
铁脚表面应清洁无锈，并经镀锌或喷砂处理，镀锌层质量符合 GB/T 3764 的规定。
6 牺牲阳极与铁脚之间的接触电阻
牺牲阳极与铁脚间的接触电阻应不大于0.001欧姆。
阳极氧化后的铝或其合金，提高了其硬度和耐磨性，可达250～500千克／平方毫米，良好的耐热性当没有供电条件或显现不经济的情况时才有应用价值。阴极保护施工，阴极保护原理，阴极保护招标适用于土壤中的牺牲阳极材料大多是镁，在海水中是锌和铝。为了使电流输出尽量保持稳定和环比阳极接地电阻，土壤中的牺牲阳极周边应采用化学填包料，主要由75%的硫酸钙，20%的膨润土和5%硫酸钠混合而成。牺牲阳极不宜埋放在焦炭中，在成组使用时，阳极间距至少应是3m。阳极顶部土壤覆盖层厚度至少为0.6m。牺牲阳极一般仅经济地应用在保护电流需要量小的构筑物上和低土壤电阻率环境中。此外为了能够测量断电电位，牺牲阳极应通过测量盒与管道相连接，牺牲阳极在交流牵引系统周围地区应用时，阳极体上的交流感应长期电压不应超过20V。阴极保护施工，阴极保护原理，阴极保护招标阳极要求：阴极保护施工，阴极保护原理，牺牲阴极保护阳极。