| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 物理性能 | 玻纤含量 | 30 | % | |||
| 比重 | ASTM D792 | 1.63 | ||||
| 熔点 | DSC | 225 | ℃ | |||
| 吸湿性 | ASTM D570 | 0.03 | % | |||
| 机械性能 | 拉伸强度 | ASTM D638 | 1200 | kg/cm2 | ||
| 拉伸伸长率 | ASTM D638 | 3.2 | % | |||
| 弯曲强度 | ASTM D790 | 1800 | kg/cm2 | |||
| 弯曲模量 | ASTM D790 | 85000 | kg/cm2 | |||
| Izod缺口冲击强度 | ASTM D256 | 8.0 | kg.cm/cm | |||
| 洛氏硬度 | ASTM D785 | 121 | R | |||
| 电气性能 | 介电强度 | ASTM D149 | 22 | KV/mm | ||
| 体积电阻率 | ASTM D257 | 1015 | Ω.cm | |||
| 表面电阻率 | ASTM D257 | 1013 | Ω | |||
| 介电常数 | 60Hz | ASTM D150 | 3.5 | |||
| 损耗因数 | 60Hz | ASTM D150 | 0.001 | |||
| 耐电弧性 | ASTM D495 | 100 | SEC | |||
| 热性能 | 热变形温度 | - | 1.8Mpa | ASTM D648 | 200 | ℃ |
| - | 0.46Mpa | ASTM D648 | 218 | ℃ | ||
| 阻燃性 | UL94 | V-0 | ||||