| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 物理性能 | 吸湿率 | 24h | ASTM D570 | 0.03 | % | |
| 玻璃纤维含量 | 30 | % | ||||
| 比重 | ASTM D792 | 1.54 | ||||
| 机械性能 | 硬度 | ASTM D785 | 90 | M | ||
| 引张伸长率 | ASTM D638 | 3.0 | % | |||
| 挠曲模数 | ASTM D790 | 3.0 | kg/cm2 | |||
| 挠曲强度 | ASTM D790 | 1800 | kg/cm2 | |||
| 挠曲强度 | ASTM D790 | 1800 | kg/cm2 | |||
| 挠曲强度 | ASTM D790 | 1800 | kg/cm2 | |||
| 引张强度 | ASTM D638 | 580 | kg/cm2 | |||
| 冲击强度 | ASTM D256 | 7 | kg.cm/cm | |||
| 挠曲模数 | ASTM D790 | 88000 | kg/cm2 | |||
| 电气性能 | 体积抵抗率 | ASTM D257 | 1015 | Ω.cm | ||
| CTI | IEC 112 | 175～250V | V | |||
| 诱电正接 | ASTM D150 | 0.01 | 60Hz | |||
| 介电常数 | ASTM D150 | 3.2 | 60Hz | |||
| 耐电弧性 | ASTM D495 | 110 | SEC | |||
| 绝缘破坏强度 | 2mm | ASTM D149 | 19 | KV/mm | ||
| 表面抵抗率 | ASTM D257 | 1013 | Ω | |||
| 热性能 | 热膨胀系数 | ASTM D696 | 3 | 10-5cm/cm℃ | ||
| 热变形温度 | - | 18.6kg/cm2 | ASTM D648 | 195 | ℃ | |
| - | 4.6kg/cm2 | ASTM D648 | 210 | ℃ | ||
| 熔点 | DSC | 225 | ℃ | |||
| 耐燃性 | 0.8mm | UL94 | V-0 | |||